STAR ZIRCONIA SHT MULTI LAYER BLANKS

AGKEM Star Zirconia SHT Multi Layer Blanks are dental ceramic materials featuring a multi-layer configuration for aesthetic dental restorations. They combine 1050 MPa reported flexural strength, 47–49% translucency, and tested biological properties for compatible dental applications.

SHT commonly refers to Super High Translucency, while Multi Layer describes the material's layered configuration. Multi-layer zirconia is generally intended to support aesthetic restorations, although the supplied specifications do not describe the exact shade gradient or number of layers.

Multi-layer zirconia blanks are generally designed to provide aesthetic variation within a single disc, potentially reducing additional characterization steps. However, the specific shade transitions and layer structure of AGKEM Star SHT Multi Layer Blanks are not detailed in the supplied specifications.

The primary distinction is the multi-layer configuration of SHT Multi Layer Blanks, which is intended for aesthetic restoration applications. The previously supplied regular SHT and current SHT Multi Layer test data report the same 1050 MPa strength and 47–49% translucency, so a performance difference cannot be established from those figures alone.

These blanks are suitable for dental labs, CAD/CAM milling centers, dental technicians, and dental prosthesis manufacturers producing compatible zirconia restorations. They are particularly relevant for dental labs focused on aesthetic anterior dental applications.
AGKEM Star Zirconia SHT Multi Layer Blanks combine 1050 MPa reported flexural strength, 47–49% translucency, 1293 HV hardness, and 6.03 g/cm³ sintered density. Their multi-layer configuration, available disc thicknesses, and reported biological test results make them a material option for aesthetic dental CAD/CAM workflows.